翻译例句
1. 熔合线和焊趾处疲劳裂纹扩展速率较其他部位大。
The fatigue crack propagation rate of the fusion line and weld toe are greater than that of the others.
2. 佛两线天然气输送管道检测与评价时，发现管道内焊趾多处开裂。
Cracks were found at internal weld toes of the pipes of Fo-Liang gas transporting line.
3. 第二种是产生于立柱翼缘与主梁翼缘连接处的坡口焊缝焊趾处的裂纹。
The second crack is a crack originating at the groove weld toe of the column flange-girder flange connection.
4. 焊趾处萌生的裂纹往往在垂直于作用应力方向沿着横向宽度在多处形成。
Cracks, growing at weld toe, tend to form at numerous sites along the transverse width perpendicular to the applied stresses.
5. 给出高强钢焊趾表面裂纹在压弯组合应力下应力强度因子及其疲劳寿命计算式。
The formulae for calculating SIF and fatigue life of surface crack at weld toe of the high-strength steel under the combination stresses have been presented.
6. 给出了高强钢焊趾表面裂纹在压弯组合应力下应力强度因子及其疲劳寿命计算式。WwW.WentiYI.com
The formulae for calculating SIF and fatigue life of surface crack at weld toe of the high-strength steel under the combination stresses were given out.
7. 使用超声波冲击焊趾来提高焊接接头及结构的疲劳强度，是国际上刚刚出现的一种新方法。
It is a new method to increasing fatigue strength of welded joints and structure by peening welded toes with ultrasonic peening equipment.
8. TIG熔修处理工艺在焊趾区引入了残余拉应力，而超声冲击在焊趾区形成了较大数值的压缩应力。
Residual extend stress is produced at weld toe by TIG dressing, while compressing stress of high values by ultrasonic peening.
9. 结果表明：锤击处理可明显强化焊接接头，特别是随焊锤击能够明显强化焊趾，提高焊件的强度和塑性。
Results shows that penning in the weakest region of welded joint may strengthen welded toe obviously, and substantially improve ductility and strengthen of weldment.
10. 提出一种对接头焊趾先进行一遍tig熔修处理，然后再实施超声波冲击的复合处理新方法用来改善焊接接头的疲劳性能。
A new compound treating method of improving fatigue performance of high-strength welded joint is that firstly treated the welded toe by TIG-dressing and then performed ultrasonic peening.
11. 数值计算结果表明：T型接头焊趾区经过TIG电弧重熔处理后，虽然能够改善焊趾的形状，但该部位仍呈拉伸残余应力状态。
The results show that after TIG arc remelting treatment, the T-joint weld toe area can improve the shape of the weld toe, however, the area till shows a tensile residual stress state.
12. 又算出了这五种形状角焊缝趾端部和焊肉中央处的表面裂纹疲劳断裂的寿命。
The fatigue life of the surface cracks of the weld toe and the central part of the welding bead are calculated.
13. 又算出了这五种形状角焊缝趾端部和焊肉中央处的表面裂纹疲劳断裂的寿命。
The fatigue life of the surface cracks of the weld toe and the central part of the welding bead are calculated.