1. 在硫化体系不变的情况下，可用硫化曲线定性比较并用胶的共硫化程度。

When the formulation of blend was unchanged, the curing curve could be used to compare the co-vulcanization qualitatively.

2. 结果表明，提高共混胶的相容性和共硫化是获得产品优异性能，从而使这一新型材料在新的领域广泛应用的关键。

The results showed that improving the blend compound"s compatibility and co-cure is the key to achieve excellent properties so that the new material will be widely used in a new field.

3. 平板硫化机主要用于天然橡胶、合成橡胶、再生橡胶以及塑料的塑炼与混炼，橡胶与塑料的共炼。

Plate vulcanizing machine is mainly used for natural rubber, synthetic rubber, recycled rubber and plastic mixing and kneading of plastic, rubber and plastic co-refining.

4. 硫化胶与沥青这种高聚物混合材料共混后，对沥青的性质会产生一定的影响。

After blending of vulcanized rubber and the asphalt mix materials of this polymer, the nature of the asphalt will have some effects.

5. 动态硫化增加了共混物中NR与HDPE相界面间的结合力。

The combination Power of phase surface between NR and HDPE in blends can be enhanced by dynamic Vulcanization.

6. 加入共交联剂，可以提高交联程度，缩短硫化时间。

Addition of co-crosslink agent increased the degree of crosslinking and shortened the vulcanization time.

7. 研究了NR/BR为70/30（质量比）时普通、半有效和有效3种硫化体系共混物的拉伸疲劳寿命和力学性能。

The fatigue failure and mechanical properties of conventional, semi-efficient and efficient curing systems of NR/BR(70/30) blend were studied.

8. 研究了共混比、硫化体系、增强剂、软化剂和硅烷偶联剂对IIR/CIIR共混胶动态力学性能的影响。

The effects of blend ratio, curing system, reinforcement agents, soften agents and silane coupling agents on dynamic mechanical properties of IIR/CIIR blends were researched.

9. 使共混胶料的耐油性、耐寒性、低压缩永久变形性能达到综合平衡，因此探讨了动态硫化工艺条件。

The dynamical vulcanization technique let properties of oil resistance, low temperature resistance and compression set of the blend turn into comprehensive equilibrium.

10. 研究了HDPE/硫化胶粉共混材料的力学性能和流动性能。

The mechanical properties and fluidity of HDPE/vulcanized rubber powder blend are studied.

11. 研究了预处理短纤维用量对乙炔炭黑填充甲基乙烯基硅橡胶（VMQ）／EPDM共混硫化胶拉伸、撕裂、耐屈挠疲劳和导电性能的影响。

The influence of the level of the pretreated short fibre on tensile strength, tear strength, flex fatigue and conductivity of the acetylene black filled VMQ/EPDM blend vulcanizate was studied.

12. 研究不同硫化体系对NBR/氯化聚醚（PCMO）共混物性能的影响。

The effect of different curing systems on the properties of NBR/PCMO blend was investigated.

13. 通过不同配方比实验，研究了杜仲胶对三元共混硫化胶性能的影响。

The effects of gutta upon the vulcanizate of ternary blends are studied via the experiments of different prescriptions.

14. 研究了PPC的添加量、硫化剂的种类及用量、硫化时间、硫化温度和添加炭黑对共混弹性体的物理力学性能、交联度的影响。

The effects of PPC content, curing agent, curing temperature, curing time and adding carbon black on the mechanical properties of the blends were studied.

15. 研究了共混时间对动态硫化EPDM/PP体系结构、静态以及动态力学性能的影响。

The effect of the blending time on the structure, the static and dynamic mechanical properties of dynamically vulcanized EPDM/PP blend was investigated.

16. 采用三羟甲基丙烷三丙烯酸酯(TMPTA)作共交联剂，研究其对EPDM的过氧化物硫化行为、力学性能及老化性能的影响。

The influence of TMPTA co curing agent on the curing behavior, the physical properties and the aging properties of the peroxide cured EPDM was investigated.

17. 结果表明，预先将聚脂短纤维和EPDM混炼制成母炼胶，然后再与PP共混进行动态硫化制备的复合材料的性能最佳。

The results showed that the blending method of premixing masterbatch of short polyester fiber and EPDM, and then blending with PP was the best method.

18. 硫化体系采用酚酸树脂2402／氯化亚锡（8／0．5）、加入一定量的增塑剂邻苯二甲酸二辛酯和补强剂高耐磨炭黑，可获得性能较好的共混体。

A blend with better properties could be obtained by adding phenolic resin 2402/tin bichloride (8/0. 5) curative and a certain level of dioctyl phthalate plasticizer and HAF reinforcing agent.

19. 用动态硫化工艺制得共混物的性能优于非动态硫化工艺制得的共混物。

The aging resistance of blends made by dynamic vulcanization was better than that of blends made by non-dynamic vulcanization.

20. 结果表明，EPDM/CIIR共混比为80/20硫化胶有较好的综合性能，比单独使用EPDM作主体材料的减震胶垫减震效果更好。

The result shows that synthesize performances of EPDM/CIIR devulcanizing blend using in shock absorption were better as its ratio was 80/20, than single EPDM.

21. 结果表明，选择酚醛树脂硫化体系、控制酚醛树脂用量为5 份以及EPDM／PP共混比为50／50，可以得到挤出表面最为光滑的共混物。

The results showed that the extrudate with the most smooth surface was obtained when 5 phr of phenolic resin and 50/50 blending ratio of EPDM/PP were used.

22. 研究了硫化体系、橡塑比对共混物性能的影响。

The effects of the curing system and the amount of POM on properties of NBR/POM blends were studied.

23. 低硫高促硫化体系S/TT/CZ可以使NBR胶料具有较低的压缩永久变形，而且赋予NBR/ECO共混胶料良好的综合性能。

The S /TT /CZ system could also decrease the compression set of NBR and endowed the NBR/ECO blend with good comprehensive properties.WWW.WenTiyI.CoM

24. 采用素炼法及共素炼法均可明显提高活化胶粉胶料硫化胶的物理机械性能；

The mechanical properties of AWRP compounds increased by the method of plastication or co-plastication.

25. 结果表明，预先将聚脂短纤维和EPDM混炼制成母炼胶，然后再与PP共混进行动态硫化制备的复合材料的性能最佳。

The effects of blending methods and equipments on the properties of short polyester fiber reinforced EPDM/PP blending thermoplastic elastomer were studied.

26. 化学性质稳定，与碳共热还原为硫化钡。

Chemical properties of stability, with a total reduction of carbon barium sulfide.

27. 几种不同防焦剂在硫黄硫化天然橡胶共混胶料中，随着促进剂的品种和几种促进剂并用的变化，在硫化系统中的作用机理和大小是不同的。

A few Kinds of anti-scorcher in NR blend cured with sulphur have a different mechanism of effect along with the change of accelerator type and blend of accelerators in curing System.

28. 几种不同防焦剂在硫黄硫化天然橡胶共混胶料中，随着促进剂的品种和几种促进剂并用的变化，在硫化系统中的作用机理和大小是不同的。

A few Kinds of anti-scorcher in NR blend cured with sulphur have a different mechanism of effect along with the change of accelerator type and blend of accelerators in curing System.